Blank for producing dental shaped parts and method for producing the shaped part

ABSTRACT

The invention relates to a blank for producing dental shaped parts, comprising a blank body ( 1 ) made of tooth restoration material, from which the shaped part can be machined using a tool ( 11, 12, 13, 14, 15 ) for removing material. The aim of the invention is to enable a reliable verification or recognition of the tool fitting or of the type and state of wear of the used tool of a machine tool for the blank. To this end, the blank has at least one gauge ( 4, 5 ), whose dimensions are such that the tool present for the machining can be identified by the gauge on the basis of its outer contour. The invention also relates to a method for producing dental shaped parts with a blank body made of tooth restoration material, from which the entire shaped part can be machined in a machining device by a tool for removing material. In order to enable a reliable verification or recognition of the tool fitting or of the type and state of wear of the used tool of a machine tool for the blank, the tool selected for the machining is, before its use, verified with regard to the outer contour thereof by using at least one gauge that is placed upon the blank.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The invention relates to a blank as defined in the claims which is to be used in the production of a dental shaped part, and to a method of producing said shaped part.

2. Description of the Related Art

EP 0 160 797 discloses a blank for the production of dental shaped parts, which blank is made up of a handle and a corpus of different materials. A reference surface on the handle can be formed in such a way that control information for the machining process depending on the characteristics of the blank, can be derived.

Another blank for the production of dental shaped parts is disclosed by DE 196 12 699. Here again, recognition of the type of blank from the geometrical shape of its contours is disclosed.

EP 0 455 854 discloses a blank, from which there can be carved a mating part to be administered to the patient, on the one hand, and an additional retaining or supporting part, on the other hand. A recess is carved into the mating part, which is shaped in such a way that it can be fitted on the retaining or supporting part.

The position of the abrasion-prone tools used for machining the blank is adjusted such that the tools are moved to engage defined reference surfaces on the blank. These reference surfaces can be on the handle, as shown in EP 0 160 797 or they can, as shown in DE 196 12 699, be positioned on the corpus of the blank or on its own reference part, which is attached to the blank at more or less arbitrary places.

The reference surfaces that are provided in the prior art are only suitable for purposes of adjustment of the tool relative to the blank.

It is an object of the invention to make it possible to reliably analyze or identify the tool equipment and/or the type and state of wear of the tool used in the machining equipment employed for machining the blank. In particular, it is intended to provide means of recognizing incorrect tool setups in grinding machines using different types of tool at the same time.

SUMMARY OF THE INVENTION

This object is achieved, according to the invention, by the features defined in the characterizing clauses of the independent claims, developments being characterized by the respective subclaims.

The advantage of a blank for the fabrication of dental shaped parts, comprising a corpus of tooth restoration material, from which, in turn, the shaped part can be made by machining, with the blank exhibiting at least one gauge that is geometrically formed in such a way that the tool used for machining is identifiable on the basis of its outer contour by means of the at least one gauge, is that the effectiveness of machining can thus be guaranteed using the intended specialty tool. Whether the blank consists of ceramics, metal, plastics, or any other dimensionally stable material is of no consequence. An incorrect tool setup can be particularly well recognized in the case of grinding machines that use different types of tool at the same time. Both grinding and milling, for example, are suitable machining processes.

The gauge is advantageously assigned to an ideal outer contour of a first tool, as this makes it possible to identify the tool that corresponds to the gauge. In addition, another tool having a different ideal outer contour from that of the first tool can be distinguished with the aid of the same gauge. In this way, not only can the tool matching the gauge be selected, but different tools can be distinguished from each other.

An advantageous shape of such a gauge can be a recess, in which the ideal outer contour of the first tool engages. Such engagement can be made possible, for example, by forming the recess such that the tool having an ideal outer contour fits it exactly.

Advantageously, the gauge exhibits a recess that corresponds to a first diameter d1 of the ideal outer contour of a first cylindrical tool, which diameter is smaller than the ideal outer contour of a second cylindrical tool having a second diameter d2. In this way, at least two tools of identical geometry but of different sizes can be distinguished from each other.

Another advantageous shape of such a recess serving as a gauge is a recess that is tapered in correspondence with the ideal outer contour of a first tapered tool, with the recess tapering to a diameter that is smaller than the smallest diameter of the ideal outer contour of a second cylindrical tool. In this way, it is also possible to distinguish tools of different geometry from each other. This principle is naturally also transferable to any other tool shapes, and can be used, for example, on tools having a rounded end.

Advantageously, the gauge is in the form of a groove or bore, since these are particularly easy to create.

It is especially advantageous when the gauge is designed in such a way that when the tool to which the gauge is assigned is moved into the gauge, the actual state of the permissible allowances of the respective tool can be identified such that the degree of wear of the tool can be assessed and, for example, a certain minimum tool quality can be prescribed. A further advantage is that it is possible to effect a reliable analysis or identification of the tool setup and/or the type of tool used in the machining equipment employed for machining the blank, and the wear condition of said tool.

Another advantage is gained when the blank comprises a handle for mounting and/or positioning the corpus of the blank in a machining device and when the gauge is provided on said handle, since thereby the gauge will remain effective throughout the entire machining operation and the corresponding tools can be checked on a continuous basis. Such identification of poor quality tools or incorrect setups will be contributory, for example, to preventing tool fracture during machining.

Alternatively, at least one gauge can be on the handle or on the corpus of the blank or on a reference area, by which means special production characteristics can be taken into consideration. In addition, at least one gauge can be at least two of the said positions.

If the gauge is designed as a universal gauge for prospective tools, advantageously various tool geometries can be checked with only one gauge. A gauge is considered to be a universal gauge if the geometrical shape of several tools can be checked with the aid of this one gauge. This requires that the shape geometry itself consists of several individual shape geometries, of which each corresponds to the tool geometry of its respective tool. By this means, it is not only possible for a more extensive tool setup to be examined with the aid of only one gauge, but it is also possible to examine the degree of wear of a number of, or if necessary all, tools with the aid of just one gauge. In this way, it will be possible to detect incorrect setup with minimum elaboration. Instead of using only one universal gauge, several universal gauges of identical or different geometrical shapes can be used if this would seem necessary, for production or control reasons for example, in order to enable the tool to be driven to the blank more quickly, for instance.

In accordance with a development, several gauges are provided for the characterization of a single tool and this single tool can be examined for more than one parameter of its condition and in particular for its deviation from an ideal condition.

The advantage of a procedure for the fabrication of dental shaped parts using a blank corpus of dental restoration material, from which the entire shaped part can be carved in a machining device by means of a tool, and the profile of the tool selected for such machining is examined before it is put to use with the aid of at least one of the gauges disposed on the blank is that it is possible to ensure, in this way, that said tool is, indeed, the correct tool for the machining operation to be carried out. This is achieved in that the actual values obtained are compared with the ideal outer contour.

A further advantage results if the tool dedicated to the gauge is driven into the gauge and the current deviation of the assigned tool from the ideal is determined, since information about the momentary tool condition can be determined in this manner each and every time the tool engages the gage(s) gauge(s). This can be done several times during an operation sequence. Thus an optimal condition and, therefore, high quality of the shaped part can be guaranteed.

Another advantage results when the degree of deviation of the actual condition of the tool from the ideal outer contour of the tool is determined and this deviation is allowed for when organizing the control of the blank machining operation. A parameter, for example, can be established for this purpose. A tool whose unsuitable condition has been recognized can, in such a case, be excluded from the machining process and new or other tools in better condition can carry out the task in hand. It is also conceivable to reduce down times by causing a change of tool to be suggested only if the machining process cannot be finished with any of the other tools that are already involved in the process. The information gained from the comparison can thus be used for a tool condition-specific control of the machining process.

All in all, it is to be emphasized that the gauges can be positioned anywhere and, advantageously, are not only provided for the selection of the tool by reproducing the negative shape of the tool intended for machining in its ideal condition, but are also available for determining the wear condition of the tool. The exact position of the gauge will be known to the machining equipment or is determined by it.

In addition, the gauge can be designed such that it can identify tools that are designated for the material.

This can, for example, be effected via the geometry or a specific machining resistance when using the tool in the known geometry of the gauge under known machining effort.

BRIEF DESCRIPTION OF THE DRAWINGS

The method of the invention is described with reference to the drawings, in which:

FIG. 1 a is a perspective view of a first blank for the fabrication of a dental shaped part with a gauge on a handle of a blank corpus,

FIG. 1 b is a perspective view of a further embodiment of a blank according to the invention with a gauge on the blank corpus,

FIG. 1 c is a perspective view of a further blank having at least one gauge on a reference surface located on the blank,

FIG. 2 a is a longitudinal cross-section of the blank of FIG. 1 a,

FIG. 2 b is a longitudinal cross-section of the blank of FIG. 1 b,

FIG. 2 c is a longitudinal cross-section of the blank of FIG. 1 c,

FIG. 3 a shows a machining tool in the form of a diamond-coated cylindrical grinder having a first diameter,

FIG. 3 b shows a machining tool in the form of a diamond-coated cylindrical grinder having a second diameter,

FIG. 3 c shows a machining tool in the form of a diamond-coated grinder having a conical point,

FIG. 3 d shows a machining tool in the form of a diamond-coated grinder having a tapered portion and a rounded conical point,

FIG. 3 e shows a machining tool in the form of a diamond-coated grinding wheel,

FIG. 4 a shows a gauge by means of which the machining tool of FIG. 3 a is checked,

FIG. 4 b shows a gauge by means of which the machining tool of FIG. 3 b is checked,

FIG. 4 c shows a gauge by means of which the machining tool of FIG. 3 c is checked,

FIG. 4 d shows a gauge by means of which the machining tool of FIG. 3 d is checked,

FIG. 4 e shows a gauge by means of which the machining tool of FIG. 3 e is checked,

FIG. 4 f shows a gauge by means of which the wear condition of the machining tool of FIG. 3 c is checked,

FIG. 5 shows a gauge that is designed as a universal gauge for checking several tools having various contours,

FIG. 6 shows a further embodiment of a gauge suitable for use as a universal gauge, and

FIGS. 7 a, 7 b show wear measurement means for a cylindrical and conical grinder respectively.

DESCRIPTION OF EXEMPLARY EMBODIMENTS OF THE INVENTION

The blank of FIG. 1 a contains a corpus 1, which can consist of a material commonly used in dental technology, e.g., a ceramic material, but also of any other dimensionally stable material such as metal or plastics, from which the shaped part will be fabricated by means of a material removal machining process. The corpus 1 of the blank is advantageously circular or rectangular in cross section. The front end of the corpus of the blank is adjoined by a cylindrical handle 2 in known manner.

The material of handle 2 can be identical with, or different from, that of the corpus 1. In the case of different materials, blank corpus 1 will be fastened to handle 2, for example by gluing. For this purpose, handle 2 exhibits, for example, a circular cylindrical flange 2 a having a diameter that is sufficient to ensure secure attachment to corpus 1, and a shaft 2 b for insertion into the machining equipment. Shaft 2 b is designed to fit into a predefined socket on the machining equipment.

In FIGS. 1 a to c, a recess 5 having gauge properties is provided. Such recesses can be provided individually or in moderate numbers at various places of the blank. Due to their gauge properties, these recesses serve to select and evaluate the individual tools, since five specific sets of data of the tool, e.g., their dimensions, state of wear, and position, can be identified with the aid of the recesses 5.

The blanks illustrated in FIGS. 2 a to 2 c are structurally comparable to the blanks of FIGS. 1 a to 1 c. According to FIG. 2 a, two gauges 4, 5 are provided on flange 2 a of handle 2 of the blank in the form of gauge recesses. In this case, the gauges are in the form of a groove and bore 4, 5 respectively. FIG. 2 b shows a blank which exhibits two gauges 4, 5 on the corpus 1 of the blank. The blank of FIG. 2 c is also structurally comparable to the blank of FIG. 1 c and comprises a mating part 6, which in this case is disposed on corpus 1 opposite handle 2. The mating part 6 can be of the same material as the corpus of the blank and can be located on the axis 7 of the handle and can itself serve to determine the size and position of the machining tool. Alternatively, any number of other locations can be considered for the mating part 6, as long as it does not impede the machining process. Moreover, it can have the cylindrical shape shown or some other shape. Two gauges 4, 5 are disposed on mating part 6 in the form of recesses, which in this figure are in the form of a groove 4 and bore 5.

With all blanks, it is essential that the position of the gauges 4, 5 on the machining equipment is known or can be unambiguously determined. This can be done, for example, by scanning.

FIG. 3 shows machining tools as used for machining corpus 1. FIGS. 3 a and 3 b show a diamond-coated cylindrical grinder or milling cutter, with the grinder 11 of FIG. 3 a exhibiting a first diameter d1 and the grinder 12 of FIG. 3 b a second diameter d2. A grinder that is designed in this way is primarily used for machining interior spaces with vertical walls. FIGS. 3 c and 3 d each show a diamond-coated grinder 13, 14 that tapers to a point. In FIG. 3 c, the end of the grinder 13 exhibits an angle δ of 45°. In FIG. 3 d the end of the grinder 14 is in the form of a cone, of which the point is rounded with a radius R. A grinder that is shaped in this way is primarily used for machining occlusion surfaces with fissures, as well as interior spaces with non-vertical walls.

FIG. 3 e shows a diamond-coated grinding wheel 15, which is used for both separation and roughing as well as for carving down to final dimensions. The edges of the grinding wheel exhibit a radius r and the wheel has a diameter d5 and a width b.

FIG. 4 shows the machining tool of FIG. 3 engaged in a gauge. FIGS. 4 a and 4 b show a diamond-coated cylindrical grinder 11, 12, and demonstrate how grinder 11 penetrates the bore-shaped gauge 5 by a distance t1, whilst the other grinder 12, because of its larger diameter, cannot penetrate gauge 5. The penetration depth t2 is in this case equal to zero, from which it can be ascertained that tool 12 is involved.

FIGS. 4 c and 4 d each show a diamond-coated grinder 13, 14 tapered to a tip as it penetrates gauge 5 in the form of a bore. The penetrations illustrated in FIGS. 4 c and 4 d of a magnitude t3 in FIG. 4 c and t4 in FIG. 4 d, serve not only to determine the ideal outer contour and thus to define the type of tool, but also provide information on the wear condition and the suitability of the respective tool for the intended machining process.

FIG. 4 e shows a diamond-coated grinding wheel 15 at a point at which grinding wheel 15 is about to move into the groove-shaped gauge 4 of FIG. 3 e on corpus 1 of the blank. This moment of penetration provides information as to whether the grinding wheel is too thick and thus unsuitable for the scheduled grinding procedure.

FIG. 4 f shows a gauge 5 that is used to detect the wear condition of the tool tip. The gauge has a conical open region 5.1, which merges into a base region 5.2. Between them is a cylindrical region 5.3. Tool 13, when new, moves into the gauge at its pointed end such that only the tip touches the base 5.2. If the tip is as worn out as on tool 13′, then the depth of penetration of its pointed end up to the point of reaching the base 5.2 or up to the point of touching the side walls of the open region 5.1 will be greater than when tool 13 is new. The amount of wear can thus be inferred from this measurement.

FIG. 5 shows a single cylindrical recess 5′ for tools 11 to 14 shown in FIGS. 3 a to 3 d that is designed as a universal gauge. The respective actual penetration depths t1′, t2′, t3′, t4′, provide information on the condition of the respective tool and thus on the suitability of the tool for the intended machining operation.

FIG. 6 shows a further single recess 5″ serving as a universal gauge. This recess includes a bore 16 having a diameter d2 and an associated possible penetration depth t2 and one having a diameter d1 and an associated possible penetration depth t2. In addition, the recess exhibits a taper 17 having a cone angle β and a further taper 18 having a cone angle {acute over (α)} for the examination of corresponding tools. Alternatively, instead of one or more angles, one or more roundings having radii R (see FIG. 3 d) that match the respective tools can be provided. The penetration depth achieved in each instance can yield information on the condition of the respective tool and thus the suitability thereof for the intended machining operation. FIGS. 7 a and 7 b show how wear measurement can be carried out. Tool 11 is furnished with a coating 19 that provides the actual cutting edges, for example the diamond coating of a grinding pin. This coating 19 exhibits an ideal outer contour 20, which is indicated by the dashed lines. However, due to the wear incurred during machining, the actual outer contour 21 of tool 11 will deviate from the ideal outer contour 20.

In the region of the end-cutting surface, the amount of wear of the coating 19 between the ideal outer contour 20 and the actual outer contour 21 is equal to the distance 6 which, with an original coating thickness of from 50 to 60 μm, can well amount to from 40 to 50 μm. The wear of the end-cutting surface can be determined by measuring the depth of penetration of tool 11 into gauge 5. FIG. 7 b shows how a gauge 5 can be used for measurement of the wear of a coated conical grinder. The conical grinder has a coating 19, which again has an ideal outer contour 20 and an actual outer contour 21. Due to the bore 16, the diameter of the used tool 13 is first identified and, due to a stop limit surface 22 having a central bore 23, the wear δ_(d) of the envelope of the cone is determined. The wear of the cone δ_(s) tip can be determined in accordance with FIG. 7 a, but can also be measured in accordance with FIG. 7 b when certain empirical values are available. For the measurement of a truncated cone point, and also of a conical grinder, a separate gauge can be provided for each diameter, and the wear measurement can, in each case, be carried out by measuring the depth of penetration into the gauge. 

1. A system comprising: first and second tools, a diameter of an end of the first tool being smaller than a diameter of an end of the second tool; and a blank from which a dental shaped part is produced, the blank including a corpus of tooth restoration material from which the dental shaped part is formed by removing material using at least one of the first and second tools, and at least one gauge in the form of a recess having at least one predetermined dimension and shape, the end of the first tool fitting into the recess wherein the recess is smaller in size than the diameter of the second tool.
 2. The system as defined in claim 1, wherein the gauge distinguishes an outer contour of the first tool from an outer contour of the second tool.
 3. The system as defined in claim 1, wherein the shape of the recess is cylindrical and a diameter of the recess is smaller than the diameter of the second tool.
 4. The system as defined in claim 1, wherein the recess is tapered to correspond at least in part to an outer contour of the first tool and the recess tapers to a diameter which is smaller than the diameter of the second tool.
 5. The system as defined in claim 1, wherein the recess is in the form of a groove or a bore.
 6. The system as defined in claim 1, wherein the recess identifies a state of permissible allowance of the first tool when the first tool engages the recess.
 7. The system as defined in claim 1, wherein the blank has a handle for positioning the corpus of the blank in machining equipment, and the recess is provided on the handle.
 8. The system as defined in claim 1, wherein the recess is located on the corpus.
 9. The system as defined in claim 1, wherein the gauge functions as a universal gauge for prospective tools.
 10. The system as defined in claim 1, wherein the blank includes a plurality of gauges, each of the plurality of gauges being designed as a recess having dimensions and a shape that correspond at least in part to an outer contour of a different one of the first and second tools.
 11. The system as defined in claim 1, wherein the gauge has a first diameter of an outer contour of the first tool, and an outer contour of the second tool does not fit into the gauge. 